Dachin PS 990
Polysiloxane coating

Main Composition

The coating consists of polyorganosiloxane resin, rheology additives, pigments/fillers, and minimal solvents. The secondary component is a curing agent.

Main Characteristics

The cured film exhibits excellent adhesion, hardness, gloss, and decorative properties, along with superior weather resistance and color/finish retention. Complies with standards: Technical Specifications for Cold-Sprayed Zinc Corrosion Protection of Bridge Steel Structures (JT/T 1266-2019), Technical Conditions for Highway Bridge Steel Structure Corrosion Protection Coatings (JT/T 722-2023), and Technical Specifications for Port Machinery Steel Structure Surface Coatings (JT/T 733-2021).

Main Applications

Designed for high-performance protective and decorative coating of steel structures in transportation vehicles, construction machinery, and critical infrastructure projects.

Technical Specifications

Film Color and Appearance	Conforms to color requirements, uniform surface with no particles, pinholes, or bubbles
Density, kg/L	1.51±0.04
Fineness, μm	≤35

Package Specifications

Component	Package Weight / kg	Package Volume / L
A	21.4	14.2
B	3.6	3.8
Total	25	18

Basic Parameters

Mix Ratio	Weight Ratio A:B = 6:1
	Volume Ratio A:B = 3.7:1
Pot Life	5℃: 5 hours; 15℃: 4.5 hours; 25℃: 4 hours
Theoretical Consumption	Approx. 20㎡/L @ 30μm dry film thickness

Recoat Interval

Temperature	Surface Dry	Hard Dry	Recommended Topcoat Recoat Interval
			Minimum	Maximum
5℃	120 minutes	16 hours	16 hours	2 days
15℃	90 minutes	10 hours	10 hours
25℃	60 minutes	6 hours	6 hours
40℃	40 minutes	4 hours	4 hours

Data based on standard film thickness applied to steel substrate.

Application

• Dachin PS 990 Polyorganosiloxane Coating is recommended for airless spray application to achieve optimal single-coat film build compared to other methods.
• Surface temperature must remain at least 3℃ above dew point with humidity <85%.
• Ensure ventilation in enclosed spaces during application.
• Mix the coating with curing agent strictly according to the ratio before use. Mix only the required quantity and use within the pot life after preparation. Stir thoroughly before use.
• Maintain tool cleanliness and dryness before and after application.
• Avoid contact with water, acids, or alkalis during mixing and application. Ensure curing agent containers are sealed tightly after use to prevent curing and material loss.
• Allow full curing for 7 days before putting the coated surface into service.

Compatible Coatings

Undercoats: Dachin EP 550 Epoxy Iron Oxide Intermediate Coat, Dachin H53-90 Cold-Sprayed Zinc Sealer, Dachin ZP 210 Zinc Phosphate Epoxy Primer.

Recommended Coats

Apply 2 coats for a dry film thickness of 60±5μm.

Surface Preparation

Clean the surface to remove oil, dust, and other contaminants. Ensure no acid/alkali residues or moisture condensation. For cured polyurethane, fluorocarbon, or epoxy coatings, lightly sand and roughen the surface before applying topcoats.

Mixing

This 2-component system (A base resin and B curing agent) requires thorough stirring with power tools separately before mixing. Strictly follow the ratio and mix again until homogeneous.

Application Methods

Application Method	Diluent	Dilution Rate	Nozzle Orifice	Pressure
Airless Spraying	Dachin Thinner X11	0-5% (by paint weight)	0.4-0.5mm	15-20 MPa
Air Spraying	Dachin Thinner X11	0-10% (by paint weight)	1.5-2.0mm	0.3-0.5 MPa
Roller/Brush	Dachin Thinner X11	0-5% (by paint weight)	-	-

Dilution rates are calculated by paint weight.